Specification | Acceptable Range | Result | Test Method | Explanations |
Penetration | 85-100 | 91 | ASTM – D5 | at 25°c , mm/10 |
Softening Point | 45-53 | 45.4 | ASTM – D36 | °c |
Ductility | 100 | >100 | ASTM – D113 | at 25°c , cm |
Solubility | 99.0 Min | 99.87 | ASTM – D2042 | in CCL4 , % |
Specific Gravity | 1.01-1.06 | 1.01 | ASTM – D70 | at 25°c |
Spot Test | Negative | Negative | T102 | in Naphtha |
Flash Point | 220 Min | 334 | ASTM – D92 | °c |
Kinematic Viscosity | …. | 287 | ASTM – D4402 | at 135°c , c.st |
Absolute Viscosity | …. | 1164 | ASTM – D4402 | at 60°c , Poises |
Test on Residue From Thin Film Oven Test (T.F.O.T) | ||||
Drop in Penetration | 20 Max | 8.9 | ASTM – D5&D6 | % |
Mass Loss | 0.2 Max | 0.11 | ASTM – D6 | Wt% |